 【Company Profile of Rongxing Group-China's Leading Supplier of Electrode Paste】

4.jpg
    Backed by over 24 years of experience of manufacturing, marketing and distributing premium carbon metallurgical products and solutions worldwide, Rongxing Group is committed to providing a range of high quality, innovative, cost-effective products, solutions and services. The main products are graphite electrode, electrode paste, graphite powder, calcined petroleum coke, carbon brick. 

    The company attaches great importance to the development, accumulation and upgrading of patented technologies, having strong equipment, process research and development capabilities and product innovation capabilities, strictly implementing international standards, industry standards, and implementing total quality management. Rongxing holds itself to the highest quality standards that control everything from incoming raw materials to final factory production. All materials are tested to ensure they meet industry standards before entering the manufacturing phase. Our maxims are uncompromising quality, outstanding customer service and operational dependability. To continually improve our products, services and our quality management system by establishing and reviewing quality objectives on a consistent basis. For large-scale projects and special solutions in particular, we offer customers a one-stop shop. Working together with both our customers and primary agents, end users will be asked to complete our Electrode and Furnace Data Form. This information will be carefully reviewed and used to determine the appropriate grade of electrode for the particular application. Our goal is to supply the most cost effective electrode for your operation, an electrode that will run without breakage and offer efficiency in production. 

    We focus on continual product development, improvement, thoughtful services and technical support. Professional technicians will visit customers regularly; Providing after-sales support; Rongxing has proven to be a reliable and qualified supplier of superior graphite and carbon products to various international operations.

【Introduction of Rongxing Electrode Paste】
2.jpg
    The electrode paste is dehydrated and melted by petroleum coke and pitch coke in a melting tank, and proportionally added to the kneading pot and kneaded, then molded and calcined. 

    It has the characteristics of low resistivity and is used as a conductive material in electric furnace equipment such as ferroalloy furnace and calcium carbide furnace. Electrode paste can be said to be a simple and technically complicated product in carbon production. After being kneaded and molded, the electrode paste became a finished product. Unlike other carbon and graphite products, when defects occur in the previous process, it can be compensated by baking, graphitization or even an impregnation process. 

    The electrode paste is calcined by the heat in the submerged arc furnace. There- fore, the consumption speed of the electrode and the calcination speed are the key to the use of the electrode paste. As the submerged arc furnace technology gradually develops toward
large-scaled and air-tightness, during the calcining process, the electrode develops from the old type opened furnace type to the closed furnace type, and the heat obtained by the electrode from the furnace is greatly reduced, which requires an increase in the sintering perfromance of the electrode paste to compensate for this deficiency.


【Application of Electrode Paste】

     Used in the electric equipment such as ferroalloys furnace, carbide furnace as a conductive material.
 

【Specification of Sealed Electrode Paste】

Ash Content 4.0%
        V.M  12.0-15.5
        Compression Strength  >18.0Mpa
Resistivity 65Ω
Density  >1.38 g/cm3
Extensibility 5-20%
 
13.jpg

【Points of Advantage of Rongxing Electrode Paste】

    Customization according to the customer's equipment and the type of ferroalloy being produced; private customization.

    With the most advanced technology, production technology and testing technology. Professional after-sales service technical support and QC team.

    The factory is in a good position and has all kinds of high-quality raw materials which can  produce electrode paste.
    
3.jpg
【Special Note for Electrode Paste】

        For electrode paste manufacturers, the two most taboo problems are soft and hard electrode breakage, of which soft breakage is even more terrible and can easily cause accidents. Hard breaking is caused by insufficient strength of the electrode paste after sintering; soft breaking is because the electrode sintering speed is not as fast as the consumption speed, and the lowering is too fast. The electrode cannot be fully sintered and cannot withstand the tensile and lateral impact of the lower part of the electrode, causing fracture. These two problems are directly related to the performance of the carbon manufacturer's electrode paste, and also related to the operation during use.

        At present, the main problem that plagues manufacturers is that the electrode paste baking speed is too slow, so some manufacturers use methods to reduce the amount of asphalt used. This method is effective to a certain extent, but the amount of bitumen is too low, resulting in poor fluidity of the electrode paste, the electrode paste is not easy to fill in the electrode barrel, and the poor density after sintering is easy to cause hard breaks. Another method is to reduce the bitumen The softening point of the electrode increases the sintering speed of the electrode, but the softening point of the asphalt can not be reduced indefinitely, because the too low softening point of the asphalt reduces the coking rate of the asphalt.

        Therefore, in addition to properly grasping the above two methods, the production of electrode paste also needs to improve the sintering speed of the electrode through the adjustment of the formula, such as appropriately adding graphite materials with good conductivity and heat transfer performance in the formula Conduction heat obtained in the furnace to speed up the roasting speed, while trying to reduce the consumption of the electrode to reduce the speed of the electrode lowering can also achieve the matching of electrode consumption and roasting.

【Contact us】

       Rongxin Carbon Products Co., Ltd.
       Contact: Manager Lou
       Address: Shuanglou Village, Mihe Town, Gongyi City
       Tel: 86 + 15290889928 (same number on WeChat & WhatsApp)
       Website: www.electrodepaste.com
 
.

Click here You can send email directly:[email protected]


Or Leave the message:

HOT SELLING

well selled in the latest days.

UHP Graphite Electrodes
Resistance:4.8-5.8
Density:>1.68
CTE:1.1-1.4
Young Modulue:9.0-13.0
Rupture Modulus:10.0-14.0
HP Graphite Electrodes
Resistance:5.8-6.6
Density:>1.62
CTE:1.4-2.2
Young Modulue:13.0-16.0
Rupture Modulus:10.0-11.0
RP Graphite Electrodes
Resistance:6.6-9.0
Density:>1.53
CTE:1.4-2.2
Young Modulue:9.0-13.0
Rupture Modulus:11.0-15.0
Goose Shaped & Trapezoid Shaped
Goose Shaped:30mm*60mm*80mm;
Trapezoid Shaped:Bottom Length14cm,Bottom Wieth 10cm;Height 9.5cm;Top Legnth 9cm,Top Width 4cm.
Ash content 2-10%
Resistivity 55-90 uΩm
V.M 10.0-15.0
Density >1.46g/cm3
Compression Strength >18Mpa
Extensibility 6-20
Carbon Electrode Paste(Cylinder)
Diameter:600mm;
Length:1000mm;
Ash content 2-10%
Resistivity 55-90 uΩm
V.M 10.0-15.0
Density >1.46g/cm3
Compression Strength >18Mpa
Extensibility 6-20
Various types of electrode paste
petroleum coke, asphalt in the melting bath dehydration, melting, in proportion to join the HunNieGuo kneading, and then formed calcined together.With the characteristics of low resistance coefficient used in the electric equipment such as ferroalloys fur
Various types of electrode paste
petroleum coke, asphalt in the melting bath dehydration, melting, in proportion to join the HunNieGuo kneading, and then formed calcined together.With the characteristics of low resistance coefficient used in the electric equipment such as ferroalloys fur
Electrode paste
petroleum coke, asphalt in the melting bath dehydration, melting, in proportion to join the HunNieGuo kneading, and then formed calcined together.With the characteristics of low resistance coefficient used in the electric equipment such as ferroalloys fur
Cylindrical electrode paste
petroleum coke, asphalt in the melting bath dehydration, melting, in proportion to join the HunNieGuo kneading, and then formed calcined together.With the characteristics of low resistance coefficient used in the electric equipment such as ferroalloys fur

Call us or Add WhatsApp